| Properties |
Method |
Unit |
Nylon 66 |
| Specific gravitiy |
ISO 1183 |
g/cm3 |
1,14 |
| Water Absorption |
DIN 53495 |
% |
2,4 |
| Chemical Resistance |
X |
X |
X |
| Max. permissible service temperature |
- |
°C |
80 |
| Min. permissible service temperature |
- |
°C |
-30 |
| Tensile strength at yeild |
ISO 527 |
MPa |
90/60 |
| Elongation at yeild |
ISO 527 |
% |
X |
| Tensile strength at break |
ISO 527 |
MPa |
X |
| Elongation at break |
ISO 527 |
% |
<40 |
| Impact Strength |
ISO 179 |
kJ/m2 |
o.B. |
| Notch Impact Strength |
ISO 179 |
kJ/m2 |
4.5/11 |
| Ball indication hardn. (Hk)/Rockwell |
ISO 1239-1 |
MPa |
160/- |
| Shore-D |
DIN 53505 |
|
X |
| Flexural strength |
ISO 178 |
MPa |
X |
| Modulus of elasticity |
ISO 527 |
MPa |
3450/1650 |
| Vicat softening temp. VST/B/50 VST/A/50 |
ISO 306 |
°C |
X |
| Heat deflection temperature HDT/B HDT/A |
ISO 75 |
°C |
X |
| Coef. of linear therm. expansion |
DIN 53752 |
K-1x 10-4 |
0,80 |
| Thermal conductivity at 20°C |
DIN 52612 |
W/(m x K) |
0,28 |
| Volume resistivity |
VDE 0303 |
x cm |
1013 / 1010 |
| Surface resistivity |
VDE 0303 |
|
<1013 / 1010 |
| Dielectric constant at 1 MHz |
DIN 53483 |
|
3,3/3.8 |
| Diel. loss factor at 1 MHz |
DIN 53483 |
|
0,02/0.6 |
| Dielectric strength |
VDE 0303 |
KV/mm |
27/18 |
| Tracking resistance |
DIN 53480 |
|
CTI600 |
| Bondability |
|
|
YES |
| Physiological indifference according |
EEC 90/128 FDA |
|
0 |
| Friction coefficient |
DIN 53375 |
|
0,35-0,42 |
| Flammability |
UL 94 |
|
X |
| UV stabilisation |
|
|
+/0 |
| Acid resistance |
|
|
X |
| Hydroxid resistance(delute) |
|
|
YES |
| Hydrocarbonat resistance |
|
|
+/0 |
| CKW resistance |
|
|
X |
| Aromatic resistance |
|
|
+/0 |
| Ketone resistance |
|
|
YES |
| Resistance against hot water |
|
|
+/0 |